<b>Attended</b>: ''Moskov'', ''Sean''. ''Justin'', ''Mikhail'', ''Jim'', ''Hovanes'', ''Eugene'', ''Pavel'', and ''Igor''. | <b>Attended</b>: ''Moskov'', ''Sean''. ''Justin'', ''Mikhail'', ''Jim'', ''Hovanes'', ''Eugene'', ''Pavel'', and ''Igor''. | ||
| − | [https://wiki.jlab.org/klproject/images/0/0c/Zinkle90.pdf] | + | The transition fluence for void swelling in irradiated pure copper is the issue as ''Bogdan'' pointed out. First of all, thank you, ''Pavel'', for sending us a nice overview ([https://wiki.jlab.org/klproject/images/0/0c/Zinkle90.pdf]). Actually, the main source of the problem is (n, alpha) and (n,t) reactions and the bottom line is to prevent a transition fluence for void swelling in irradiated pure copper, we have to (1) keep the temperature of our Cu radiator below 200°C (2) use Cu with 2%Be and/or 3.5%Ti. |
Revision as of 06:35, 25 May 2021
Attended: Moskov, Sean. Justin, Mikhail, Jim, Hovanes, Eugene, Pavel, and Igor.
The transition fluence for void swelling in irradiated pure copper is the issue as Bogdan pointed out. First of all, thank you, Pavel, for sending us a nice overview ([1]). Actually, the main source of the problem is (n, alpha) and (n,t) reactions and the bottom line is to prevent a transition fluence for void swelling in irradiated pure copper, we have to (1) keep the temperature of our Cu radiator below 200°C (2) use Cu with 2%Be and/or 3.5%Ti.